Article Navigation >  LASER TECHNOLOGY  > 2002 >  26(3): 189-191

Citation:
shu

Fatigue growth rate of laser shock processed metal sheet

  • 1.

    Beijing Aeronautical Manufacturing Technology Research Institute, Beijing, 100024;

  • 2.

    Beijing University of Aeronautics and Astronautics , Beijing, 100083

  • Received Date: 2001-05-15
    Accepted Date: 2001-09-03
  • Compact tension(CT) specimens of superalloy with thickness of 1.5mm and a high strength steel sheet with thickness of 1.7mm are processed by laser shock,with three spots with diameter of 6mm overlapped along the extension line of precut crack.The fatigue crack growth rates of laser shock processed specimens are compared with those without LSP.The results show that effects of laser shock strengthening have much difference along the crack growth line,the fatigure growth rates can not be fitted by the Paris formula,but laser shock processing can decrease the fatigue crack growth rate in whole distincctly.
  • 加载中
  • [1]

    Peyre P,Fabbro R,Berthe L et al. J Laser Application,1996,8(3):135～141.
    [2]

    Chu J P,Rigsbee J M,Banas G et al. Metallurgical & Materials Transactions A,1995,26(A):1507～1517.
    [3]

    Eisner K,Lang A,Schutte K et al. SPIE,1996,2789:274～280.
    [4]

    Obata M,Sano Y,Mukai N et al. Effect of Laser Peening on Residual Stress and Stress Corrosion Cracking for TYPE 304Stailless Steel. The 7th International Conference on Shot Peening,Institute of Precision Mechanics,Warsaw,Poland,1999:387～394.
    [5] 高镇同主编.疲劳性能试验设计和数据处理.北京:北京航空航天大学出版社,1999.
  • 加载中
通讯作者: 陈斌, bchen63@163.com
  • 1. 

    沈阳化工大学材料科学与工程学院 沈阳 110142

  1. 本站搜索
  2. 百度学术搜索
  3. 万方数据库搜索
  4. CNKI搜索
Get Citation
PDF
XML

Article views(2833) PDF downloads(609) Cited by()

Proportional views

Fatigue growth rate of laser shock processed metal sheet

  • 1. Beijing Aeronautical Manufacturing Technology Research Institute, Beijing, 100024;
  • 2. Beijing University of Aeronautics and Astronautics , Beijing, 100083
  • Received Date: 2001-05-15
  • Accepted Date: 2001-09-03
  • Available Online: 2002-05-25

Abstract: Compact tension(CT) specimens of superalloy with thickness of 1.5mm and a high strength steel sheet with thickness of 1.7mm are processed by laser shock,with three spots with diameter of 6mm overlapped along the extension line of precut crack.The fatigue crack growth rates of laser shock processed specimens are compared with those without LSP.The results show that effects of laser shock strengthening have much difference along the crack growth line,the fatigure growth rates can not be fitted by the Paris formula,but laser shock processing can decrease the fatigue crack growth rate in whole distincctly.

    HTML

Reference (5)

Catalog

    Copyright © Laser Technology. 蜀ICP备10038222号-1

    Address：No. 7, Section 4, Renmin South Road, Chengdu, Sichuan Province, China Postal Code：610041  Telephone：028-68011091/68011046  Email： jgjs@vip.163.com,  jgjs@sina.com

    Supported by: Beijing Renhe Information Technology Co. Ltd  support: info@rhhz.net

    /

    DownLoad:  Full-Size Img  PowerPoint
    Return
    Return